Thermoforming is a manufacturing process for thermoplastic sheet or film. The sheet or film is heated between infrared, natural gas, or other heaters to its forming temperature. Then it is stretched over or into a temperature-controlled, single-surface mold. Cast or machined aluminum is the most common mold material, although epoxy, wood and structural foam tooling are sometime used for low volume production. The sheet is held against the mold surface unit until cooled. The formed part is then trimmed from the sheet. The trimmed material is usually reground, mixed with virgin plastic, and reprocessed into usable sheet [1]. There are several categories of thermoforming, including vacuum forming, pressure forming, twin-sheet forming, drape forming, free blowing, and simple sheet bending.


Thin and thick gauge thermoforming

There are two general thermoforming process categories. Sheet thickness less than 1.5 mm (0.060 inches) is usually delivered to the thermoforming press in rolls. Thin gauge roll fed thermoforming applications are dominated by rigid or semirigid disposable packaging. Sheet thickness greater than 3 mm (0.120 inches) is usually delivered to the forming press cut to final dimensions and stacked on pallets. Heavy or thick gauge, cut sheet thermoforming applications are primarily used as permanent structural components. There is a small but growing medium gauge market that forms sheet 1.5 mm to 3 mm in thickness.

Heavy gauge forming depended on convection oven heating of the sheet and draping of the sheet over male, female or paired molds. Aircraft windscreens and machine gun turret windows spurred the advance of heavy gauge forming technology during WWII. Heavy gauge parts are used as cosmetic surfaces on permanent structures such as automobiles, refrigerators, spas and shower enclosures, and electrical and electronic equipment.

Engineering

Thermoforming can fabricate thin walled parts with large areas, using relatively inexpensive, single-sided tooling. Its deficiencies – variable wall thickness, added cost of sheet and trim regrind, and extensive trimming – have been offset by the ability to economically produce a few, thick walled parts or very many thin walled parts.

Thermoforming has benefited from applications of engineering technology [3]. Infrared radiation is the primary method of heating sheet. The softened sheet is arithmetically treated as a rubbery elastic membrane as it stretched mechanically or pneumatically into or onto a cooled single surface rigid mold. Finite element analysis is used to predict local wall thickness of the formed sheet. Heavy gauge sheet is trimmed with multiaxis routers adapted from the woodworking industry.

Industry

The more than USD10 billion North American market has traditionally been ¾ thin gauge and ¼ heavy gauge. In 2003 there were about 150 thin gauge thermoformers in North America. Sixty percent formed proprietary products. Thirty percent were custom formers and 10 percent were OEMs with in-house forming capability. There were nearly a dozen thin gauge formers having annual sales of at least USD100 million. The largest had annual sales in excess of USD1,000 million. There were about 250 heavy gauge formers in North America. Nearly all were custom formers. Only two or three heavy gauge formers had annual sales of more than USD100million. The largest had annual sales of about USD140 million [2].

References

  1. J.L. Throne, Understanding Thermoforming, Hanser Gardner Publications, Inc., Cincinnati OH, 1999.
  2. The Industrial Thermoforming Business: Review and Outlook, Plastics Custom Research Services, Advance NC, 2004.
  3. J.L. Throne, Technology of Thermoforming, Hanser Verlag, Munich, 1996.
  4. Florian, J., "Practical Thermoforming", 1996, ISBN: 0824797620
  5. Gruenwald, G, "Thermoforming: A Plastics Processing Guide", 1998, ISBN: 1566766257

External links

See also

Manufacturing (from Latin manu factura, "making by hand") is the use of tools and labor to make things for use or sale. The term may refer to a vast range of human activity, from handicraft to high tech, but is most commonly applied to industrial production, in which raw
..... Click the link for more information.
For other uses, see Plastic (disambiguation).
A thermoplastic is a plastic that melts to a liquid when heated and freezes to a brittle, very glassy state when cooled sufficiently.
..... Click the link for more information.
Infrared (IR) radiation is electromagnetic radiation of a wavelength longer than that of visible light, but shorter than that of radio waves. The name means "below red" (from the Latin infra, "below"), red being the color of visible light with the longest wavelength.
..... Click the link for more information.
Vacuum forming, commonly known as Vacuforming, is a simplified version of thermoforming, whereby a sheet of plastic is heated to a forming temperature, stretched onto or into a single-surface mold, and held against the mold by applying vacuum between the mold surface and the
..... Click the link for more information.
Blow molding or blow moulding (see spelling differences) is a manufacturing process by which hollow plastic parts are formed. In general, there are three main types of blow molding; Extrusion Blow Molding, Injection Blow Molding, and Stretch Blow Molding.

History

U.
..... Click the link for more information.
For other uses, see Plastic (disambiguation).
A thermoplastic is a plastic that melts to a liquid when heated and freezes to a brittle, very glassy state when cooled sufficiently.
..... Click the link for more information.
Vacuum forming, commonly known as Vacuforming, is a simplified version of thermoforming, whereby a sheet of plastic is heated to a forming temperature, stretched onto or into a single-surface mold, and held against the mold by applying vacuum between the mold surface and the
..... Click the link for more information.
Microthermoforming is the abbreviation for microscopic or microscale thermoforming, or, more precisely, for thermoforming of microproducts or microstructure products. Microstructure products means products that have structures in the micrometre range and have their technical
..... Click the link for more information.
Injection molding (British variant spelling: moulding) is a manufacturing technique for making parts from both thermoplastic and thermosetting plastic materials in production.
..... Click the link for more information.
Blister pack is a term for several types of pre-formed clear plastic packaging used for small consumer goods.

The two primary components of a blister pack are a pre-formed plastic blister and a printed paperboard card which has a heat-seal coating.
..... Click the link for more information.
Blow molding or blow moulding (see spelling differences) is a manufacturing process by which hollow plastic parts are formed. In general, there are three main types of blow molding; Extrusion Blow Molding, Injection Blow Molding, and Stretch Blow Molding.

History

U.
..... Click the link for more information.
Packaging is the science, art and technology of enclosing or protecting products for distribution, storage, sale, and use. Packaging also refers to the process of design, evaluation, and production of packages.
..... Click the link for more information.


This article is copied from an article on Wikipedia.org - the free encyclopedia created and edited by online user community. The text was not checked or edited by anyone on our staff. Although the vast majority of the wikipedia encyclopedia articles provide accurate and timely information please do not assume the accuracy of any particular article. This article is distributed under the terms of GNU Free Documentation License.
Herod_Archelaus


page counter